POROPHORE-57 azobisisobutyronitrile is used as a pore agent, initiator in manufacture of nytron fibre and for initiating of process of chlorination of dichloroethane and for other purposes. It is received by oxidation of hydrazonitrile of isobutyric acid with chlorine.
Appearance: white or white with greyish shade fine-crystalline powder.
During storage, is able to become caked.

Melting point, within	100 - 103°C
Gas number, no less than	140 cm³/g
Mass fraction of substances that are not soluble in isopropyl alcohol, no more than	0,2 %
Mass fraction of humidity at sieve with mesh No.2	Absent

VASELINE
Paste of Porophore-57 (azobisisobutyronitrile), vaseline, can be used during production of tyres.
Appearance: dense paste-like paste of various colours.

Gas number, no less than	85 cm³/g
Mass fraction of humidity, no more than	0,1%

Hydrazodicarbonamide (HDCA) is a semi-produc of manufacture of Porophore-51. Appearance: white crystalline substance.

Mass fraction of hydrazine nitrogen	23,4 - 24,0%
Mass fraction of humidity, no more than	0,1%
Alkalinity	Absent
Acidity	Absent

Quick-drying alkyd-phenolic resin AMF30x60 is used for manufacture of quick-drying primers and primer-enamels. Ensures high oil-and-gas resistance and anticorrosion resistance.

Conditional viscosity by viscometer B3 - 4 at t° (20±0,5)°C	110 - 170 s (50% solution in xylene)
Fat content	30%
Acid number, no more than	20 mg KOH/g
Colour by iodometric scale, no more than	30 mg l2⁄100 cm³
Delivery conditions	60% solution in xylene

Quick-drying alkyd-urethane resin ATU60ws52 is used for manufacture of quick-drying paint-and-varnish materials of increased hardness and wear resistance for interior work.

Conditional viscosity by viscometer B3 - 4 at t° (20±0,5)°C	150 - 300 s
Fat content	60%
Acid number, no more than	15 mg KOH⁄g
Colour by iodometric scale, no more than	30 mg l2⁄100 cm³
Delivery conditions	52% solution in xylene

Quick-drying alkyd resin ATB30⁄60 is used for manufacture of quick-drying primers.

Conditional viscosity by viscometer B3 - 4 at t° (20±0,5)°C	150 - 240 s
Fat content	30%
Acid number, no more than	20 mg KOH⁄g
Delivery conditions	60% solution in xylene

Alkyd resin AT40d70 is used for production carbamide paint-and-varnish materials of acid hardening, nitrocellulose varnishes and enamels. Resin does not contain aromatic solvents.

Brookfield viscosity at t° (20±0,5)°C	2000 - 3300 mPa.s
Fat content	40%
Acid number, no more than	20 mg KOH⁄g
Colour by iodometric scale, no more than	15 mg l2⁄100 cm
Delivery conditions	70% solution in methoxypropylene glycol

Resin, carbamide-formaldehyde, KM-411-03 EB is used for manufacture of paint-and-varnish materials of acid hardening. Resin does not contain aromatic solvents, has low content of free formaldehyde.

Colour by iodometric scale, no more than	2 mg l2 ⁄ 100 cm³
Mass fraction of non - volatile substances	50±2
Conditional viscosity by viscometer B3-4 with nozzle diameter 4 mm at	90 - 180 s
Mass faction of free formaldehyde, no more than	0,5%
Acid number, no more than	2,5 mg KOH ⁄ g

Resin BMS-86 is used for manufacture of paint-and-varnish materials. It is copolymer of butyl methacrylate, methyl methacrylate and methacrylic acid in mix of solvents of butyl acetate and white spirit. Appearance: homogeneous transparent liquid of yellowish and yellowishgreen colour. Opalescence is allowed.

Conditional viscosity by viscometer B3-4 with nozzle diameter 4 mm at	40 - 90 s
Mass faction of non - volatile	50 - 56%
Acid number, no more than	2,5 mg KOH⁄g

Fatty alkyd resin ATI70ws55 is used for manufacture of quick-drying atmosphere-resistant varnishes and enamels. Resin is made based on aliphatic solvents.

Conditional viscosity by viscometer B3-4 with nozzle diameter 4 mm at t° (20±0,5)0C	200 - 320 s
Fat content	70%
Acid number, no more than	20 mg KOH⁄g
Colour by iodometric scale, no more than	20 mg l2⁄100 cm³
Drying time ar presence of siccative (2%, LB -2), no mo than	6 hours
Delivery conditions	55% solution in white spirit

Fatty alkyd resin AM60ws55 is used for manufacture of weather-resistant paintand- varnish materials used for coating of wood, metal and other surfaces during work inside and outside premises. Forms a film that does not become yellow in course of time.

Conditional viscosity by viscometer B3-4 with nozzle diameter 4 mm at t° (20±0,5)0C	200 - 320 s
Fat content	60%
Acid number, no more than	15 mg KOH⁄g
Colour by iodometric scale, no more than	20 mg l2⁄100 cm³
Delivery conditions	55% solution in white spirit

Fatty alkyd resin AT65ws55 is used for manufacture of weather-resistant paintand- varnish materials used for coating of wood, metal and other surfaces during work inside and outside premises.

Conditional viscosity by viscometer B3-4 with nozzle diameter 4 mm at t° (20±0,5)0C	150 - 300 s
Fat content	65%
Acid number, no more than	15 mg KOH⁄g
Colour by iodometric scale, no more than	15 mg l2⁄100 cm³
Delivery conditions	55% solution in white spirit

Fatty alkyd resin ATL70ws60 is used for manufacture of unpigmented systems for impregnation and decorative finish of wooden urfaces during work inside and outside premises.

Conditional viscosity by viscometer B3-4 with nozzle diameter 4 mm at t° (20±0,5)0C	120 - 250 s
Fat content	70%
Acid number, no more than	20 mg KOH⁄g
Colour by iodometric scale, no more than	15 mg l2⁄100 cm³
Delivery conditions	55% solution in white spirit

Fatty alkyd resin AMG55ws55 is used for manufacture of pigmented systems for impregnation and decorative finish of wooden urfaces during work inside and outside premises.

Conditional viscosity by viscometer B3-4 with nozzle diameter 4 mm at t° (20±0,5)0C	300 - 600 s
Fat content	59%
Acid number, no more than	15 mg KOH⁄g
Colour by iodometric scale, no more than	15 mg l2⁄100 cm³
Delivery conditions	55% solution in white spirit

Polyester resin E-101 is used for manufacture of unshrinkable polyurethane materials that do not contain solvents.

Hydroxyl number	225 - 250 mg KOH⁄g
Delivery conditions	Resin that does not contain solvent

Polyester resin E-101H is used for manufacture of unshrinkable polyurethane materials that do not contain solvents.

Hydroxyl number	325 - 350 mg KOH⁄g
Delivery conditions	Resin that does not contain solvent

Resin, alkyd-urethane, ATU58ws54 is solution of alkyd-urethane copolymer in white spirit or oil solvent C4 150⁄200. Resin, alkyd-urethane, ATU58ws54 is intended for manufacture of quickdrying weather-resistant paint-and-varnish materials of increased hardness and wear resistance, used for painting of railway vans, means of municipal transport and other equipment.

Appearance:	transparent liquid. Insignificant opalescence is allowed.
Colour by iodometric scale, no darker than	20 mg l2⁄100 cm³
Mass fraction of non - volatile substances	53±1%
Brookfield viscosity at t° (20±0,5) 0C	1000 - 2000 mPa.s
Acid number (in terms of 100 % resin), no more than	15 mg KOH⁄g
Duration of drying up to grade 3 at t°(20±2)0C, no more than	360 min

Resin, acrylic, LB-85p⁄60T is solution of copolymer of styrene and methacrylates in toluene and is intended for manufacture of road-marking paints with increased wear resistance and atmosphere resistance.

Appearance	yellowish transparent iquid without mechanical impurities.Insignificant opalescence is allowed
Brookfield viscosity at t° (20±0,5)	10000 - 20000 mPa.s
Acid number (in terms of 100% resin)	5 - 10 mgKOH/g
Mass fraction of non - volatile substances	60±2 %

Resin, acrylic, LB-85p⁄50T is solution of copolymer of styrene and methacrylates in toluene and is intended for manufacture of road-marking paints with increased wear resistance and atmosphere resistance.

Appearance	yellowish transparent iquid without mechanical impurities.Insignificant opalescence is allowed
Brookfield viscosity at t° (20±0,5)	1500 - 4500 mPa.s
Acid number (in terms of 100% resin)	5 - 10 mgKOH/g
Mass fraction of non - volatile substances	50±2 %